Ti -6AL-7Nb tytanowy pręt

Ti -6AL-7Nb Titanium Rod

Ti -6AL-7Nb Titanium Rod is α+β titanium alloy: it is a two-phase alloy, with good comprehensive properties, good microstructure stability, good toughness, plasticity and high temperature deformation properties, can be better hot pressure processing, quenching, aging to strengthen the alloy.  The strength after heat treatment is about 50% ~ 100% higher than that after annealing.  High strength at high temperature, can work at 400℃ ~ 500℃ temperature for a long time, its thermal stability is inferior to α titanium alloy.  

Specification	Dia.: 4mm-100mm       Length: 50mm-6000mm
Standard	ASTM F1295
Technique	Forging, Machining
Surface	Polished/Bright
Application	Medical implants

Mechanical Property of Ti-6AL-7Nb Titanium Rod

Grade	Tensile   strength, Mpa         (min)	Yield   strength,       MPa (min)	Elongation,   % (min)	Reduction of Area，           %   （min）
Ti-6AL-7Nb	900	800	10	25

Chemical composition

Chemical conposition
Material	Ti	Al	Nb	Fe, max	C, max	N, max	H, max	O, max
Ti-6Al-7Nb	Bal	5.5-6.5	6.5-7.5	0.25	0.08	0.08	0.009	0.2